Silicon Bricks

Silica fire bricks, as the name suggests, are mainly composed of SiO2( mass percent is above 93%). High temperature performance of silica bricks mainly depends on SiO2 content, impurity content, mineral composition and so on. The higher SiO2 content, the higher refractoriness of alumina silica bricks. Mineral composition of silica bricks are tridymite, cristobalite, residue quartz and glass  phase. Silica refractory bricks properties are closed related to SiO2 crystalline phase transformation.

RS Brand Silica Fire Bricks Advantages

High purity raw materials, low impurity content.

Strict production craft control.

True density is below 2.35g/cm3, small residual expansion rate.

Various species of silica fire bricks can be customized.

1. Coke Furnace Silica Fire Bricks

Coke furnace silica firebricks primary crystalline phase is tridymite. Silica refractory bricks account for 60%~70% the total amount of refractory materials used in modern coke furnaces. The main application parts of silica bricks are regenerator wall, ramp, combustion chamber, carbonization chamber, furnace top and so on.

Coke furnace silica fire bricks properties

1.high refractoriness under load. 

2.High thermal conductivity.

3.Good thermal shock resistance.

4.Good high temperature volume stability.

2.Coke Furnace Silica Bricks Specification

Item

JLGZ-1

JLGZ-2

JLGZ-3

JLGZ-4

SiO2 % ≥

94.6

95.38

95.6

96.0

Fe2O3 % ≤

1.12

1.13

0.27

0.40

Al2O3 %

0.75

0.70

0.89

0.90

0.2Mpa refractoriness under load  

1640

1655

1671

1660

Apparent porosity % ≤

22.6

17.5

22.8

19.4

Cold crushing strength Mpa

59.0

80.0

27.5

60.0

True density g/m3

2.31

2.32

2.33

/

Bulk density g/cm3

1.79

1.91

1.79

1.85

Linear change rate %

1.18

1.18

1.26

1.30

 

2. Glass Furnace Silica Bricks

Glass furnace silica bricks main composition is tridymite, they are used to line glass tank furnace high temperature part. Glass furnace silica bricks feature in: good  high temperature volume stability, won’t cause furnace deformation due to temperature fluctuation, won’t pollute glass liquid, strong resistance to chemical corrosion, low volume density and so on.    

Glass Furnace Silica Bricks Specification

Item

BG-96a

BG-96b

BG-95a

BG-95b

SiO2 % ≥

96

96

95

95

Fe2O3 % ≤

0.8

1.0

1.2

1.2

0.2Mpa refractoriness under load  

≥1680

≥1670

≥1660

≥1650

Apparent porosity % ≤

22

22

22

22

Cold crushing strength Mpa

35

35

35

35

True density g/m3

≤2.34

≤2.34

≤2.35

≤2.35